This table is provided as an information service by Diversified Enterprises.
This table highlights polar/dispersion and acid—base breakouts of surface free energy, as well as Hansen Solubility Parameters and radius of interaction, for a variety of polymers. For all columns except polymer name, CAS #, and total Hansen Solubility Parameter (δ) the first row of data for each material is the average of surveyed values; the second row shows the standard deviation, with the number of data points (n) in parentheses. For n = 1, no standard deviation figure is shown. Click on any column's footnote for details. Click on any polymer name for original research results. An analogous table, which includes contact angle data, can be seen here. Comments on methodology and the like can be found here.
This table can be sorted by column — just click on the column header as desired to re-order this printable table. Click on any footnote for additional information.
Some print software will automatically scale this page so that it prints well with “portrait” orientation. If your printer doesn't have this feature, you will want to change your print set-up to “landscape” orientation prior to printing.
print this sort order (table and references only - will open in new browser window)
Surface Free Energy Components by Polar/Dispersion and Acid—Base Analyses; and Hansen Solubility Parameters for Various Polymers
![]() |
Polar/Dispersion | ![]() |
Acid-Base | ![]() |
Hansen Parameters | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Name(1) ![]() ![]() |
CAS #(2)![]() ![]() |
γS(3) ![]() ![]() |
γSd(4) ![]() ![]() |
γSP(5)![]() ![]() |
γS(6)![]() ![]() |
γSLW(7)![]() ![]() |
γSAB(8)![]() ![]() |
γS+ (9)![]() ![]() |
γS- (10)![]() ![]() |
δ(11)![]() ![]() |
δD(12)![]() ![]() |
δP(13)![]() ![]() |
δH(14)![]() ![]() |
Ro(15)![]() ![]() |
|||
![]() |
![]() |
![]() |
|||||||||||||||
Nylon 6,12 | 24936-74-1 | 67.0 | 62.0 | 4.7 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
2-Hydroxyethyl methacrylate (HEMA, ethylene glycol monoacrylate) | 867-77-9 | 56.8 | 36.3 | 20.5 | - | - | - | - | - | - | - | - | - | - | |||
1.20(2) | 0.49(2) | 0.71(2) | |||||||||||||||
Polyacrylamide | 9003-05-8 | 52.3 | 26.5 | 25.8 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyacetylene (polyethyne) | - | 51.5 | 48.2 | 3.4 | - | - | - | - | - | - | - | - | - | - | |||
0.71(2) | 1.77(2) | 1.06(2) | |||||||||||||||
Nylon 2 (polyglycine) | 25718-94-9 | 50.1 | 27.9 | 22.2 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polypropylene isophthalate | - | 49.3 | 35.1 | 14.2 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Nylon 4 | 24938-56-5 | 48.5 | 27.8 | 20.7 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polybutylene isophthalate | - | 47.8 | 34.9 | 12.9 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyimide (PI) | 25038-81-7 | 47.0 | 38.2 | 8.8 | 44.0 | 42.5 | 1.5 | 0.1 | 6.0 | - | - | - | - | - | |||
8.49(2) | 16.8(2) | 8.27(2) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||||||
Polyethersulfone (PES) | 25154-01-2 | 47.0 | 40.0 | 7.0 | - | - | - | - | - | 21.0 | 18.3 | 8.2 | 6.4 | 6.3 | |||
-(1) | -(1) | -(1) | 0.91(6) | 3.10(6) | 2.33(6) | 2.61(6) | |||||||||||
Polyphenylene sulfide (PPS) | 26125-40-6 | 46.8 | 44.0 | 2.8 | - | - | - | - | - | 19.8 | 18.7 | 5.3 | 3.7 | 6.7 | |||
3.29(3) | 3.50(3) | 0.71(3) | -(1) | -(1) | -(1) | -(1) | |||||||||||
Polysulfone (PSU) | 25135-51-7 | 46.6 | 30.4 | 16.2 | - | - | - | - | - | 21.5 | 18.5 | 8.5 | 7.0 | 9.4 | |||
-(1) | -(1) | -(1) | 2.17(3) | 2.61(3) | 1.12(3) | 1.69(3) | |||||||||||
Polyxylylene (parylene) | - | 46.3 | 45.7 | 0.6 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polybutylene terephthalate (PBT) | 26062-94-2 | 46.0 | 42.0 | 4.1 | 47.1 | 45.8 | 1.3 | 0.8 | 0.6 | - | - | - | - | - | |||
0.24(4) | 2.83(4) | 2.92(4) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||||||
Polyphenylene oxide (PPO) | 25134-01-4 | 46.0 | 36.0 | 10.0 | - | - | - | - | - | 20.1 | 17.9 | 3.1 | 8.5 | 8.6 | |||
-(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | |||||||||||
Cellophane | 9005-81-6 | 45.4 | 29.8 | 15.6 | - | - | - | - | - | 28.5 | 16.1 | 18.5 | 14.5 | 7.3 | |||
-(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | |||||||||||
Polyvinylidene chloride (PVDC, Saran) | 9002-85-1 | 45.3 | 40.4 | 4.9 | 40.3 | 40.4 | -0.1 | 0.0 | 2.6 | 23.1 | 19.0 | 9.6 | 9.0 | 5.8 | |||
0.38(4) | 2.93(4) | 2.91(4) | -(1) | -(1) | -(1) | -(1) | -(1) | 1.98(2) | 0.64(2) | 1.70(2) | 2.62(2) | ||||||
Poly(L-alanine) | 25191-17-7 | 45.2 | 36.0 | 9.2 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Epoxies | - | 45.0 | 37.2 | 7.8 | - | - | - | - | - | 24.1 | 19.2 | 10.9 | 9.6 | 11.1 | |||
4.63(5) | 4.68(5) | 7.00(5) | 2.53(13) | 2.37(13) | 2.66(13) | 3.98(13) | |||||||||||
Nylon 6,6 | 32131-17-2 | 44.8 | 36.3 | 9.8 | 40.2 | 36.9 | 3.3 | 1.5 | 12.1 | 25.8 | 17.2 | 9.9 | 16.5 | 4.4 | |||
3.07(8) | 5.63(9) | 4.03(8) | 3.61(2) | 0.71(2) | 2.90(2) | 2.11(2) | 13.5(2) | 1.11 | 1.10 | 6.80 | 1.24 | ||||||
Polyethylene terephthalate (PET) | 25038-59-9 | 43.7 | 36.6 | 7.2 | 45.3 | 42.6 | 1.8 | 0.3 | 3.7 | 20.8 | 18.7 | 6.3 | 6.7 | 6.5 | |||
3.42(16) | 4.64(16) | 3.42(16) | 0.78(2) | 2.83(2) | 0.71(2) | 0.21(2) | 1.06(2) | 1.25(8) | 2.03(8) | 2.80(8) | 3.36(8) | ||||||
Polychloroprene | 9010-98-4 | 43.6 | 38.8 | 4.8 | - | - | - | - | - | - | - | - | - | - | |||
0.00(2) | 0.14(2) | 0.14(2) | |||||||||||||||
Acrylonitrile butadiene styrene (ABS) | 9003-56-9 | 43.6 | 35.8 | 8.0 | 38.6 | 39.4 | -0.8 | 0.9 | 3.7 | 19.2 | 17.0 | 5.7 | 6.8 | 9.4 | |||
4.83(5) | 2.77(5) | 2.55(5) | 4.81(2) | 0.00(2) | 4.88(2) | 0.14(2) | 2.76(2) | 0.92(2) | 4.17(2) | 0.49(2) | 2.19(2) | ||||||
Polymethyl methacrylate (PMMA, acrylic, plexiglas) | 9011-14-7 | 43.5 | 35.9 | 7.8 | 42.2 | 41.6 | 0.6 | 0.0 | 11.1 | 21.3 | 17.9 | 10.1 | 5.4 | 11.0 | |||
2.88(14) | 4.09(13) | 3.79(13) | 2.97(11) | 2.36(11) | 0.89(11) | 0.04(11) | 5.84(11) | 1.37(5) | 4.46(5) | 3.73(5) | 4.63(5) | ||||||
Polycarbonate (PC) | 24936-68-3 | 43.4 | 38.2 | 5.2 | - | - | - | - | - | 22.2 | 19.6 | 8.8 | 5.7 | 10.2 | |||
8.21(3) | 9.24(3) | 3.69(3) | 1.75(3) | 2.58(3) | 1.04(3) | 4.06(3) | |||||||||||
Polyethylene oxide (PEO, PEG, polyethylene glycol) | 25322-68-3 | 42.8 | 30.8 | 12.1 | 45.1 | 44.3 | 0.8 | 0.02 | 58.0 | - | - | - | - | - | |||
0.07(2) | 0.21(2) | 0.14(2) | 1.59(4) | 1.34(4) | 1.60(4) | 0.03(4) | 10.2(4) | ||||||||||
Nylon 6 (polycaprolactum, aramid 6) | 25038-54-4 | 42.7 | 33.1 | 9.6 | 45.3 | 42.5 | 2.8 | 0.2 | 9.6 | 20.3 | 17.0 | 3.4 | 10.6 | 5.1 | |||
6.08(2) | 2.69(2) | 3.39(2) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||
Polyetheretherketone (PEEK) | 29658-26-2 | 42.1 | 36.2 | 5.9 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Ethyl methacrylate (EMA) | 97-63-2 | 42.0 | 38.8 | 3.2 | - | - | - | - | - | - | - | - | - | - | |||
1.06(2) | 0.42(2) | 0.64(2) | |||||||||||||||
Cellulose acetate (CA) | 9004-35-7 | 42.0 | 31.0 | 11.1 | 43.5 | 39.0 | 4.5 | 0.3 | 22.2 | 23.5 | 17.1 | 13.1 | 9.4 | 10.6 | |||
5.44(2) | 1.84(2) | 3.61(2) | 6.42(4) | 4.20(4) | 3.25(4) | 0.33(4) | 2.71(4) | 1.58(4) | 4.41(4) | 3.81(4) | 2.96(4) | ||||||
Polystyrene (PS) | 9003-53-6 | 41.7 | 37.0 | 5.0 | 36.9 | 37.9 | -0.9 | 0.1 | 2.2 | 23.9 | 22.8 | 5.8 | 4.3 | 12.7 | |||
1.24(8) | 3.47(9) | 2.84(8) | 5.80(3) | 4.32(3) | 1.68(3) | 0.20(3) | 2.72(3) | -(1) | -(1) | -(1) | -(1) | ||||||
Poly(hexachlorobutadiene) | - | 41.5 | 40.7 | 0.8 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polymethyl acrylate (PMA) | 25087-26-7 | 41.4 | 35.6 | 5.8 | - | - | - | - | - | - | - | - | - | - | |||
0.85(4) | 4.12(4) | 4.45(4) | |||||||||||||||
Aluminum foil (b) | 7429-90-5 | 41.2 | 31.7 | 9.5 | - | - | - | - | - | - | - | - | - | - | |||
2.47(2) | 0.57(2) | 1.91(2) | |||||||||||||||
Polyvinyl chloride (PVC) | 9002-86-2 | 40.1 | 37.4 | 2.8 | 39.8 | 38.7 | 1.0 | 0.1 | 3.1 | 20.0 | 16.8 | 8.9 | 6.1 | 8.5 | |||
3.80(9) | 3.93(10) | 2.36(9) | 4.76(6) | 4.33(6) | 0.96(6) | 0.15(6) | 2.31(6) | 1.65(5) | 1.95(5) | 1.78(5) | 3.94(5) | ||||||
Polyurethanes | - | 39.3 | 30.8 | 8.6 | 30.0 | 30.9 | -0.9 | 0.02 | 10.0 | 22.8 | 18.8 | 10.0 | 8.2 | 9.8 | |||
2.60(8) | 3.63(8) | 3.95(8) | -(1) | -(1) | -(1) | -(1) | -(1) | 1.53(11) | 2.54(11) | 3.09(11) | 3.48(11) | ||||||
Polyoxymethylene (POM, polyacetal, polymethylene oxide) | 24969-26-4 | 39.0 | 26.2 | 12.8 | - | - | - | - | - | - | - | - | - | - | |||
7.99(2) | 6.15(2) | 1.84(2) | |||||||||||||||
Polyvinyl fluoride (PVF) | 24981-14-4 | 38.6 | 34.0 | 4.6 | 37.5 | 35.6 | 1.9 | 2.8 | 6.0 | - | - | - | - | - | |||
2.85(5) | 5.72(5) | 4.38(5) | 1.30(3) | 2.08(3) | 0.85(3) | 4.73(3) | 6.62(3) | ||||||||||
Nylon 12 | 24937-16-4 | 38.2 | 33.1 | 5.2 | 41.3 | 37.0 | 4.3 | 0.6 | 7.6 | 22.2 | 18.5 | 8.1 | 9.1 | 6.3 | |||
3.46(2) | 3.96(2) | 0.42(2) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||
Polyvinyl acetate (PVA) | 9003-20-7 | 37.7 | 24.8 | 13.0 | 44.5 | 42.6 | 1.9 | 0.04 | 22.3 | 25.7 | 20.9 | 11.3 | 9.7 | 13.7 | |||
2.89(5) | 1.65(5) | 1.53(5) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||
Polyethyl acrylate (PEA) | 9003-32-1 | 37.0 | 30.6 | 6.4 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyethyl methacrylate (PEMA) | 9003-42-3 | 35.9 | 26.9 | 9.0 | - | - | - | - | - | 20.0 | 17.5 | 8.5 | 4.7 | 9.6 | |||
-(1) | -(1) | -(1) | 1.34(3) | 0.62(3) | 3.82(3) | 1.99(3) | |||||||||||
Ethylene-propylene-diene-monomer (EPDM) | 25038-36-2 | 35.5 | 29.7 | 5.8 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyvinylidene fluoride (PVDF) | 24937-79-9 | 34.4 | 25.7 | 8.7 | 30.5 | 28.6 | 1.9 | 10.5 | 0.08 | 23.2 | 17.0 | 12.1 | 10.2 | 4.1 | |||
4.17(4) | 4.64(4) | 4.81(4) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||
Polyethylene (PE) | 9002-88-4 | 34.2 | 32.8 | 1.4 | 31.7 | 31.5 | 0.2 | 0.1 | 0.9 | 17.6 | 16.8 | 3.8 | 3.8 | 6.6 | |||
2.45(19) | 2.89(19) | 1.73(19) | 2.86(10) | 2.93(10) | 0.27(10) | 0.19(10) | 1.39(10) | 0.88(7) | 1.94(7) | 2.52(7) | 2.84(7) | ||||||
Polyvinyl proprionate | 25035-84-1 | 34.0 | 26.5 | 7.5 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyisobutylene (PIB, butyl (rubber) | 9003-27-4 | 33.6 | 33.6 | 0.0 | 25.0 | 25.0 | 0.0 | 0.0 | 0.0 | 17.1 | 16.4 | 1.7 | 4.7 | 7.9 | |||
-(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | 1.26(6) | 2.15(6) | 2.08(6) | 2.46(6) | ||||||
Poly n-butyl methacrylate (PnBMA) | 95608-33-7 | 32.3 | 27.3 | 5.0 | - | - | - | - | - | 18.4 | 16.0 | 6.2 | 6.6 | 9.5 | |||
1.56(5) | 2.59(5) | 1.78(5) | -(1) | -(1) | -(1) | -(1) | |||||||||||
Poly n-butyl acrylate | 9003-49-0 | 32.2 | 28.6 | 3.6 | - | - | - | - | - | - | - | - | - | ||||
2.12(2) | 2.55(2) | 0.42(2) | |||||||||||||||
Polytetramethylene oxide | - | 31.9 | 27.4 | 4.5 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polytetrahydrofuran (PTHF) | 25190-06-1 | 31.9 | 27.2 | 4.7 | - | - | - | - | - | - | - | - | - | - | |||
0.00(2) | 0.28(2) | 0.28(2) | |||||||||||||||
Polypropylene glycol (PPG, polypropylene oxide) | 25322-69-4 | 31.7 | 31.3 | 0.4 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyvinyl butyrate | - | 31.1 | 25.8 | 5.3 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Poly iso-butyl methacrylate (PIBMA) | 9011-15-8 | 30.9 | 26.3 | 4.7 | - | - | - | - | - | 20.0 | 18.3 | 4.9 | 6.3 | 9.4 | |||
0.00(2) | 0.49(2) | 0.49(2) | 2.11(3) | 0.93(3) | 5.12(3) | 2.10(3) | |||||||||||
Thermoplastic polyolefin (TPO) | - | 30.9 | 28.5 | 2.3 | - | - | - | - | - | - | - | - | - | - | |||
3.45(11) | 2.80(11) | 3.63(11) | |||||||||||||||
Polyvinyl hexadecanoate | - | 30.9 | 29.8 | 1.1 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Poly t-butyl methacrylate (PtBMA) | 25189-00-9 | 30.5 | 26.5 | 4.0 | - | - | - | - | - | - | - | - | - | - | |||
0.00(2) | 0.42(2) | 0.42(2) | |||||||||||||||
Polypropylene (PP) | (a) | 30.1 | 27.7 | 2.4 | 32.0 | 31.7 | 0.3 | 0.2 | 0.4 | 18.0 | 17.7 | 2.9 | 1.2 | 6.2 | |||
2.42(11) | 2.46(11) | 2.45(11) | 3.99(8) | 3.56(8) | 0.76(8) | 0.45(8) | 0.76(8) | 0.46(2) | 2.80(2) | 1.71(2) | 1.76(2) | ||||||
Poly 2-ethylhexyl acrylate | 9003-77-4 | 30.1 | 28.9 | 1.3 | - | - | - | - | - | - | - | - | - | - | |||
0.90(3) | 1.57(3) | 0.78(3) | |||||||||||||||
Poly(hexyl methacrylate) | 25087-17-6 | 30.0 | 27.6 | 2.5 | - | - | - | - | - | - | - | - | - | - | |||
0.00(2) | 0.78(2) | 0.78(2) | |||||||||||||||
Polychlorotrifluoroethylene | 9002-83-9 | 29.5 | 22.6 | 6.9 | - | - | - | - | - | 16.5 | 15.6 | 2.5 | 4.7 | 5.8 | |||
1.78(3) | 1.19(3) | 2.89(3) | 2.10(3) | 1.46(3) | 2.44(3) | 1.56(3) | |||||||||||
Polyvinyl dodecanoate | - | 29.1 | 27.8 | 1.3 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyvinyl hexanoate | - | 28.9 | 25.1 | 3.8 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyvinyl decanoate | - | 28.9 | 27.1 | 1.8 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Polyvinyl octanoate | - | 28.7 | 26.5 | 2.2 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Paraffin | 8002-74-2 | 28.1 | 28.1 | 0.0 | - | - | - | - | - | - | - | - | - | - | |||
3.71(7) | 3.71(7) | 0.00(7) | |||||||||||||||
Polytrifluoroethylene | 24980-67-4 | 27.5 | 22.0 | 5.4 | 25.4 | 23.1 | 2.3 | 1.8 | 0.7 | - | - | - | - | - | |||
3.65(3) | 2.10(3) | 3.20(3) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||||||
Polydiethylsiloxane (PDES) | 63148-61-8 | 25.7 | 23.8 | 1.9 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Hexatriacontane | 630-06-8 | 23.7 | 23.6 | 0.1 | - | - | - | - | - | - | - | - | - | - | |||
6.71(3) | 6.78(3) | 0.12(3) | |||||||||||||||
Polytetrafluoroethylene (PTFE) | 9002-84-0 | 22.2 | 21.3 | 0.9 | 20.8 | 19.9 | 0.9 | 0.1 | 1.6 | 16.7 | 16.2 | 1.8 | 3.4 | 3.9 | |||
2.54(9) | 2.71(10) | 0.96(9) | 0.99(2) | 0.35(2) | 1.34(2) | 0.20(2) | 2.26(2) | -(1) | -(1) | -(1) | -(1) | ||||||
Polydimethylsiloxane (PDMS) | 9016-00-6 | 205 | 19.2 | 1.3 | - | - | - | - | - | - | - | - | - | - | |||
1.16(6) | 1.48(6) | 0.66(6) | |||||||||||||||
Fluorinated ethylene polypropylene (FEP) | 25067-11-2 | 19.9 | 17.1 | 2.8 | 17.9 | 17.9 | 0.0 | 0.0 | 0.0 | 19.6 | 19.0 | 4.0 | 3.0 | 4.0 | |||
2.90(3) | 2.66(3) | 2.51(3) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | -(1) | ||||||
Poly(heptadecafluorooctyl methacrylate) | - | 15.3 | 13.9 | 1.4 | - | - | - | - | - | - | - | - | - | - | |||
-(1) | -(1) | -(1) | |||||||||||||||
Poly(hexafluoropropylene) | - | 14.9 | 13.6 | 1.3 | - | - | - | - | - | - | - | - | - | - | |||
2.10(3) | 1.48(3) | 1.55(3) | |||||||||||||||
Polyepichlorohydrin | 24969-06-0 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly(dimethylaminoethylmethacrylate) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polybutadiene | 9003-17-2 | - | - | - | - | - | - | - | - | 18.0 | 17.5 | 2.3 | 3.4 | 6.6 | |||
-(1) | -(1) | -(1) | -(1) | ||||||||||||||
Polyvinyl pyrrolidone (PVP) | 9003-39-8 | - | - | - | 46.0 | 43.4 | 2.6 | 0.2 | 22.5 | - | - | - | - | - | |||
3.61(2) | 0.00(2) | 3.61(2) | 0.28(2) | 10.2(2) | |||||||||||||
Polyvinyl formal | 63450-15-7 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyvinyl ethyl ether (polyethoxyethylene) | 25104-37-4 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyvinyl butyral | 63148-65-2 | - | - | - | - | - | - | - | - | 24.6 | 19.1 | 9.5 | 12.2 | 10.0 | |||
0.92(3) | 4.50(3) | 1.65(3) | 1.53(3) | ||||||||||||||
Polyvinyl alcohol (PVOH) | 25213-24-5 | - | - | - | 42.0 | 42.0 | 0.0 | 0.0 | 37.0 | 25.2 | 14.7 | 14.1 | 14.9 | 10.5 | |||
-(1) | -(1) | -(1) | -(1) | -(1) | 2.51(4) | 2.13(4) | 2.18(4) | 1.38(4) | |||||||||
Polystearyl methacrylate | 25639-21-8 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly n-propyl methacrylate | 2210-79-9 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly(phosphazene) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyphenyl methacrylate | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyoctyl methacrylate | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly(nonafluoroisobutyl acrylate) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polymethylphenylsilylene | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polymethylphenylsiloxane | 9005-12-3 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly a-methyl styrene | 25014-31-7 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly(4-methyl pentene-1) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polymethacrylonitrile (PMAN) | 25067-61-2 | - | - | - | - | - | - | - | - | 23.7 | 17.2 | 14.4 | 7.6 | 3.8 | |||
-(1) | -(1) | -(1) | -(1) | ||||||||||||||
Polylauryl methacrylate | 25719-52-2 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyisoprene (PIP) | 9003-31-0 | - | - | - | - | - | - | - | - | 18.4 | 18.1 | 2.4 | 2.3 | 10.3 | |||
2.32(3) | 1.40(3) | 2.66(3) | 3.40(3) | ||||||||||||||
Poly(2-hydroxyethyl methacrylate) | 24249-16-5 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly(heptafluoroisopropyl methacrylate) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly(heptafluoroisopropyl acrylate) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Poly 2-ethylhexyl methacrylate | 25719-51-1 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyetherimide (PEI) | 61128-46-9 | - | - | - | - | - | - | - | - | 19.8 | 17.7 | 6.0 | 6.4 | 4.8 | |||
1.07(5) | 1.14(5) | 2.43(5) | 1.70(5) | ||||||||||||||
Polybenzyl methacrylate | 25085-83-0 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Polyacrylonitrile (PAN) | 25014-41-9 | - | - | - | - | - | - | - | - | 27.4 | 21.7 | 14.1 | 9.1 | 10.9 | |||
-(1) | -(1) | -(1) | -(1) | ||||||||||||||
Phenoxy resin | 26402-79-9 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Nylon 11 | 25587-80-8 | - | - | - | - | - | - | - | - | 20.5 | 17.0 | 4.4 | 10.6 | 5.1 | |||
-(1) | -(1) | -(1) | -(1) | ||||||||||||||
Nylon 10,10 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Nylon 9,9 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Nylon 8,8 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Nylon 7,7 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Nylon 6,10 | 9008-66-6 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Nitrocellulose (cellulose nitrate) | 9004-70-0 | - | - | - | 45.1 | 44.8 | 0.3 | 0.01 | 13.3 | 23.5 | 16.2 | 14.1 | 9.5 | 10.7 | |||
0.14(2) | 0.21(2) | 0.35(2) | 0.01(2) | 3.75(2) | 1.06(2) | 0.85(2) | 1.06(2) | 1.13(2) | |||||||||
Nafion | 31175-20-9 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Ethyl cellulose | 9004-57-3 | - | - | - | 28.6 | 27.4 | 1.2 | 0.04 | 8.6 | 20.4 | 19.0 | 5.6 | 4.9 | 7.9 | |||
-(1) | -(1) | -(1) | -(1) | -(1) | 1.56(2) | 1.84(2) | 1.41(2) | 2.83(2) | |||||||||
Eicosane | 112-95-8 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Cellulose triacetate | 9012-09-3 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Cellulose acetate butyrate (CAB) | 9004-36-8 | - | - | - | - | - | - | - | - | 22.2 | 17.2 | 13.8 | 2.8 | 12.6 | |||
-(1) | -(1) | -(1) | -(1) | ||||||||||||||
Aramid (Kevlar) | 26125-61-1 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
Amorphous fluoropolymer (Teflon AF) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
(a) Atactic PP CAS #9003-08-0; isotactic PP CAS #25085-53-4
(b) Aluminum foil, while obviously not a polymer, is included due to
its widespread use in package converting and other industries.
(1) Names which are most widely used to describe the material
or family of materials (e.g., polyurethanes and epoxies) at hand are
preferred here. Commonly used acronyms and synonyms are also shown.
(2) CAS (Chemical Abstract Series) numbers are shown where
available. In a number of instances, more than one CAS number is assigned
to a given polymer — in some cases the details and nuances of these
divergences are not at all clear. We have tried to reference the CAS
number which appears to have the widest use with reference to the solid
state properties of the given polymer.
(3) γs: Total surface free energy in mJ/m2 (equivalent
to dynes/cm), as reported in polar/dispersion analyses.
(4) γsd: Dispersion component of surface
free energy in mJ/m2 (equivalent to dynes/cm), as reported
in polar/dispersion analyses.
(5) γsp: Polar component of surface
free energy in mJ/m2 (equivalent to dynes/cm), as reported
in polar/dispersion analyses.
(6) γs: Total surface free energy in mJ/m2 (equivalent
to dynes/cm), as reported in acid—base analyses.
(7) γsLW: Lipschitz—van der Waals
(non-polar) component of surface free energy in mJ/m2 (equivalent
to dynes/cm), as reported in acid—base analyses.
(8) γsAB: Lewis acid—base interaction
component of surface free energy in mJ/m2 (equivalent to dynes/cm),
as reported in acid—base analyses.
(9) γs-: Base polarity (electron-donor)
component of surface free energy in mJ/m2 (equivalent to dynes/cm),
as reported in acid—base analyses.
(10) γs+: Acid polarity (electron-acceptor)
component of surface free energy in mJ/m2 (equivalent to dynes/cm),
as reported in acid—base analyses.
(11) δ: Total Hansen solubility parameter (square root of
the sum of squares of the average values for dispersion, polar, and hydrogen
bonding components), in MPa1/2 (equivalent to joules/cubic
centimeter; 2.0455 x (cal/cc)1/2) @ 20-25oC (293.15-298.15
K). All data from Hansen Solubility Parameters: A User's Handbook,
2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.
(12) δD: Hansen dispersion solubility parameter,
in MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x
(cal/cc)1/2) @ 20-25oC (293.15-298.15 K). All data
from Hansen Solubility Parameters: A User's Handbook, 2nd Ed.,
C.M. Hansen, CRC Press, Boca Raton, FL, 2007.
(13) δP: Hansen polar solubility parameter, in
MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)1/2)
@ 20-25oC (293.15-298.15 K). All data from Hansen Solubility
Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca
Raton, FL, 2007.
(14) δH: Hansen hydrogen bonding solubility parameter,
in MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x
(cal/cc)1/2) @ 20-25oC (293.15-298.15 K). All data
from Hansen Solubility Parameters: A User's Handbook, 2nd Ed.,
C.M. Hansen, CRC Press, Boca Raton, FL, 2007.
(15) Ro: Interaction radius. All data from Hansen
Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen,
CRC Press, Boca Raton, FL, 2007.